Processing, Microstructures and Properties of Ultra-High Strength, Low Carbon and V-Bearing Dual-Phase Steels Produced on Continuous Galvanizing Lines

Wu, Yingjie (2017) Processing, Microstructures and Properties of Ultra-High Strength, Low Carbon and V-Bearing Dual-Phase Steels Produced on Continuous Galvanizing Lines. Master's Thesis, University of Pittsburgh. (Unpublished)

This is the latest version of this item.

[img]
Preview
PDF
Download (8MB) | Preview

Abstract

One of the most popular elements in weight reduction programs in the automotive industry is high strength zinc coated dual-phase steel produced on continuous hot dipped galvanizing lines. The high strength is needed for mass reduction, while the protective zinc coating is needed to prevent corrosion of the thin gage cold rolled steel. The present study was aimed to explore an optimized way to produce such dual-phase steels with ultra-high tensile strength (UTS > 1280MPa), good global ductility (TE > 18%), excellent local ductility (sheared-edge ductility, HER > 40%) and products of UTS × TE > 22000 MPa × %, conforming to data of AHSS Generation III steel. A steel of this kind is referred to as a third-generation advanced high strength steel. By altering chemical compositions (0.15wt.% carbon), pre-annealing conditions (different hot band coiling temperatures and cold reductions), annealing conditions (different intercritical annealing temperatures) and annealing paths (standard galvanizing or supercool processing), this study set out to investigate the effects of these factors on the microstructures and mechanical properties of dual-phase steels. Results showed that the stored energy of cold rolled steel with 0.15wt.% carbon was much higher than that of carbon containing 0.1wt.% carbon, generating numerous lattice defects during deformation and providing more driving force for formation of austenite and recrystallization of ferrite during the intercritical anneal. In addition, it was found that the volume fraction of martensite increased with the combination of low coiling temperature, high cold reduction, and high annealing temperature, thereby increasing the tensile strength. Furthermore, the microstructural analysis and tensile testing results and showed that the tensile strength of dual-phase steel with 0.15Wt.% carbon, combined with the ultrafine microstructures (average ferrite grain sizes reached 1-2µm) could approach 1300MPa without loss of ductility and with hole expansion ratios, in some cases, reaching 35%. Since the relative hardness of the hard martensite and soft ferrite is important in controlling sheared-edge ductility, the nanohardness results of these phases were measured. It was revealed that the martensite hardness decreased with increasing volume fraction, at a given carbon content, indicating the tensile strength was independent of the martensite hardness. Other mechanical properties, such as yield strength, YS/UTS ratio, hardness and work hardening behavior, of dual-phase steels controlled by the factors mentioned above were correlated to the microstructural features. The hypothesis that the bulk carbon content would be a major factor in controlling the strength of these steels was vindicated by the results of this study.


Share

Citation/Export:
Social Networking:
Share |

Details

Item Type: University of Pittsburgh ETD
Status: Unpublished
Creators/Authors:
CreatorsEmailPitt UsernameORCID
Wu, YingjieYIW85@pitt.eduYIW85
ETD Committee:
TitleMemberEmail AddressPitt UsernameORCID
Thesis AdvisorDeArdo, Anthonydeardo@pitt.edu
Committee MemberNettleship, Iannettles@pitt.edu
Committee MemberSmolinski, Patrickpatsmol@pitt.edu
Committee MemberOyler, Johnoyler1@pitt.edu
Date: 25 September 2017
Date Type: Publication
Defense Date: 11 July 2017
Approval Date: 25 September 2017
Submission Date: 27 June 2017
Access Restriction: No restriction; Release the ETD for access worldwide immediately.
Number of Pages: 105
Institution: University of Pittsburgh
Schools and Programs: Swanson School of Engineering > Materials Science and Engineering
Degree: MS - Master of Science
Thesis Type: Master's Thesis
Refereed: Yes
Uncontrolled Keywords: DP steels; Ultra-high strength; HER
Date Deposited: 25 Sep 2017 20:51
Last Modified: 25 Sep 2017 20:51
URI: http://d-scholarship.pitt.edu/id/eprint/32691

Available Versions of this Item

  • Processing, Microstructures and Properties of Ultra-High Strength, Low Carbon and V-Bearing Dual-Phase Steels Produced on Continuous Galvanizing Lines. (deposited 25 Sep 2017 20:51) [Currently Displayed]

Metrics

Monthly Views for the past 3 years

Plum Analytics


Actions (login required)

View Item View Item